A Kossel microdiffraction experimental set up is under development inside a Scanning Electron Microscope (SEM) in order to determine the crystallographic orientation as well as the inter- and intragranular strains and stresses on the micron scale, using a one cubic micrometer spot. The experimental Kossel line patterns are obtained by way of a CCD camera and are then fully indexed using a home-made simulation program. The so-determined orientation is compared with Electron Back-Scattered Diffraction (EBSD) results, and in-situ tests are performed inside the SEM using a tensile/compressive machine. The aim is to verify a 50MPa stress sensitivity for this technique and to take advantage from this microscope environment to associate microstructure observations (slip lines, particle decohesion, crack initiation) with determined stress analyses.