The aim of this study is to investigate the applicability of titanium matrix composites (TMCs) sleeve to Al alloys die-casting. Ti and 1.88 mass% B4C were prepared for the synthesis of 10 vol% (TiC+TiB) hybrid TMCs. In-situ synthesis and net-shape forming of TMCs were carried out in a vacuum induction melting furnace. The synthesized (TiC+TiB) TMCs were examined using scanning electron microscopy, an electron probe micro-analyzer, X-ray diffraction and transmission electron microscopy. The resistance-ability of (TiC+TiB) TMCs to molten Al alloys attack was also examined. Their reactions were carried out in a furnace at 993 K for times varying from 0 to 1200 s. In the case of conventional sleeve material, H13 steel, there were severe interfacial reactions and erosion after 60 s. On the other hand, the resistance of (TiC+TIB) TMCs to interfacial reactions and erosion by molten A380 alloy was significantly increased.