The improvement of the mechanical behaviour of high performance steels brings about a renewed interest for the work hardening rate resulting from deformation-induced martensitic transformation or mechanical twinning. Even if these mechanisms are known for quite a long time, the deformation - transformation interactions that they induce is not yet fully characterised and understood. This study aims at characterising the microstructure evolution of a Fe-Mn steel grade during straining thanks to TEM and high resolution OIM. Particular patterns of austenite - epsilon and alpha' martensite are found.