We present a depth-selective 2D-ACAR and two-detector Doppler broadening study on Au nanocrystals in monocrystalline MgO(100), produced in sub-surface layers by ion implantation and subsequent thermal annealing to temperatures beyond the stability range of vacancy clusters in MgO. In contrast to the case of Li nanocrystals, it was found that positrons do not trap inside the Au nanocrystals, but only in defects at the nanocrystal-to-host interface (attached vacancy clusters). This is interpreted in terms of the positron affinity of Au, MgO and the defects.