Two qualitatively different interfaces can be encountered in TiAl intermetallics: crystallographic rotational interfaces between parallel lamellae and grain boundaries between differently oriented lamellar colonies. The effect of these crystal boundaries on propagation of plastic deformation is discussed and various occurring phenomena are described. Such effects are decisive for the strength and ductility of these technologically advanced materials.