Magnesium alloys are ideal candidates to benefit from equal channel angular extrusion (ECAE) because of their poor forming characteristics due to a hcp structure. In this study, ECAE processing was applied to ZK31 and AZ31 magnesium alloys under various conditions. The grain size of as-ECAE specimens decreases with decreasing the processing temperature, however, the grain size decreases slightly with increasing number of repetitive processing. Both the tensile strength and 0.2% proof stress of as-ECAE specimens are high when processed at low temperature, but the elongation is high when processed at high temperature. Crystal orientation is different in the two alloys and it also varies according to the processing temperature for the two alloys. The difference of the crystal orientation influences the tensile properties, especially 0.2% proof stress.