Flow shifts and changes in microstructure were investigated for superplastic deformation of 7475 Al alloy. The recently proposed internal variable theory of structural superplasticity has been applied to the results of mechanical test. Deformed microstructure was observed using a TEM to check the validity of the constitutive relations. Accommodation mechanism for grain boundary sliding was also examined through the microchemical analysis of deformed microstructures.