Nanocrystalline Silicon (Si) embedded Ni-Ti composite anode materials are synthesized by using two-stage high-energy mechanical milling (HEMM). The overall composition of the Si and NiTi (Nitinol) powders are 65 at.% and 35 at.%. The effects of crystal size, crystal structure, and microstructure on the electrochemical properties of the nanocomposite powders are examined through X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, electrochemical test and nano-indentation test. The capacities of the coin cells produced with the 6 and 10 h milled powders are 711 and 553 mAh g(-1), respectively, after the 52nd cycle. The efficiencies of the coin cells produced with the 6 and 10 h milled powders continue to maintain 97.2 and 97.5%, respectively, until 52nd cycle. Coin cells produced with 10 h milled powders show relatively low capacity fading, which are attributed to the nanocomposite structure comprised of Si nanocrystals embedded into amorphous Ni-Ti matrix phase. Coin cell of 10 h milled powders reveals the reduced number of voids. Therefore, it is believed that Si embedded Ni-Ti nanocomposite using a two-stage high energy mechanical milling can be a promising candidate for high performance Si based anode materials. (C) 2013 Elsevier B.V. All rights reserved.