We have investigated the change in the electronic structure of LixMn0.5Fe0.5PO4 through the charge process, especially in the transition metal partial DOS using X-ray absorption and resonant photoemission spectroscopy measurements. The oxidation reaction between Fe2+ and Fe3+ proceeds while the 0.5 Li ions are extracted from LiMn0.5Fe0.5PO4. Moreover, comparing resonant photoemission spectra of LixMn0.5Fe0.5PO4 with those of LixFePO4, we have found that both spectral line-shapes are almost identical, suggesting that the strong localization of the Fe 3d states in the LiMn0.5Fe0.5PO4 system. On the other hand, in Mn 2p-3d X-ray absorption and resonant photoemission spectra, the Mn oxidation reaction from Mn2+ to Mn3+ partially occurs and Mn 3d states of LixMn0.5Fe0.5PO4 remain almost unchanged through the charge reaction. Reflecting the difference in the strength of the interaction between the transition metal Fe or Mn ions and the oxygen ions, it is suggested that although the oxidation from Fe2+ to Fe3+ proceeds largely on Fe ions during the charge reaction from x = 1.0 to 0.5, the charge compensation for the electron exchange mainly occurs not only at the Mn ions but also at the poly-anion sites during the charge reaction from x = 0.5 to (C). 2012 Elsevier B.V. All rights reserved.