The chemical compatibility of sealing glass is of great importance for Solid oxide fuel cell (SOFC). In this work, the interfacial reaction between sealing glass and Cr-containing interconnect alloy is characterized by reacting Cr2O3 powders with a representative SrO-containing glass crystallized by different heat-treatment schedules. The crystalline structure and crystalline content of sealing glass are determined by X-ray diffraction. The results show that the fraction of Cr6+ decreases from 39.8 +/- 1.9% for quenched glass to 8.2 +/- 0.4% for glass crystallized at 900 degrees C for 2 h. In addition, the interfacial reaction can be further reduced with increasing crystallization temperature and time as well as the addition of nucleation agent (TiO2). The formation of some Sr-containing crystalline phases, Sr2SiO4 and Sr(TiO3), contributes to the improvement of chemical compatibility of sealing glass, in agreement with the results of thermodynamic calculations. (c) 2012 Elsevier B.V. All rights reserved.