An alkali silicate glass (SCN-1) is being evaluated as a candidate sealant for solid oxide fuel cell (SOFC) applications. The glass contains about 17 wt.% alkalis (K + Na) and has low glass transition and softening temperatures. It remains vitreous and compliant after sealing without substantial crystallization, as contrary to conventional glass-ceramic sealant. The glassy nature and low characteristic temperatures can reduce residual stresses and result in the potential for crack healing. In a previous study, the glass was found to have good thermal cycle stability and was chemically compatible with yttria stabilized zirconia (YSZ) coating during short term testing. In this study, the compliant glass was further evaluated in a more realistic way in that the sealed couples were first isothermally aged for 1000 h followed by thermal cycling. High temperature leakage was measured. Chemical compatibility was also investigated with powder mixtures to enhance potential interfacial reaction. In addition, interfacial microstructure was examined with scanning electron microscopy and evaluated with regard to the leakage and chemical compatibility results. Overall the compliant sealing glass showed desirable chemical compatibility with YSZ coated metallic interconnect of minimum reaction and hermetic behavior at 700-750 degrees C in dual environment. (C) 2011 Elsevier B.V. All rights reserved.