Porous SiO2 separator is prepared by pressing followed by sintering process. The SiO2 separator has a high porosity of 45% and good mechanical strength. After the liquid electrolyte is infiltrated, the separator exhibits quite high ionic conductivities, and the ion conductivity reaches 0.35 mS cm(-1) at -20 degrees C. More importantly, the hydrophilic SiO2 separator has an advantage over the polymer separator in the electrolyte infiltration and retention. The LiMn2O4/Li cell using the SiO2 separator shows higher discharge capacity, rate capacity, and better low-temperature properties than that using the commercial polymer separator. Furthermore, the SiO2 separator can alleviate the capacity fading of the LiMn2O4 at high temperature, implying that the SiO2 separator is very promising to be applied in the lithium-ion batteries. (C) 2013 Elsevier B.V. All rights reserved.