In this study, a novel ternary heterojunction n-ZnO/p-Cu2O/n-TiO2 nanotube arrays (n-ZnO/p-Cu2O/n-TNA) nanophotocatalyst with a sandwich-like nanostructure was constructed and applied for the photoelectrocatalytic (PEC) degradation of typical PPCPs, tetracycline (TC). The ternary heterojunction n-ZnO/p-Cu2O/n-TNA was obtained by depositing Cu2O on the surface of TNA via sonoelectrochemical deposition (SED) and subsequently building a layer of ZnO onto the p-Cu2O/n-TNA surface through hydrothermal synthesis. After being deposited by the Cu2O, the absorption-band edge of the p-Cu2O/n-TNA was obviously red-shifted to the visible region (to 505 nm), and the band gap was reduced from its original 3.20 eV to 2.46 eV. The band gap absorption edge of the ternary n-ZnO/p-Cu2O/n-TNA is similar to that of p-Cu2O/n-TN and extends the visible spectrum absorption to 510 nm, corresponding to an E-g value of about 2.43 eV. Under illumination of visible light, the photocurrent density of the ternary heterojunction n-ZnO/p-Cu2O/n-TNA electrode at 0.5 V (vs. Ag/AgCl) was more than 106 times as high as that of the pure TNAs electrode, 3.6 times as high as that of the binary heterojunction p-Cu2O/n-TNA electrode. The degradation of TC indicated that the ternary heterojunction n-ZnO/p-Cu2O/n-TNA electrode maintained a very high photoelectrocatalytic activity and excellent stability and reliability. Such kind of ternary heterojunction electrode material has a broad application prospect not only in pollution control but also in many other fields. (C) 2013 Elsevier B.V. All rights reserved.