The leaching of gold from the scrap mobile phone PCBs by electro-generated chlorine as an oxidant and its recovery by ion exchange process was investigated. The leaching experiments were carried out by employing separate leaching reactor connected with the anode compartment of a Cl-2 gas generator. The leaching of gold increased with increase in temperature and initial concentration of chlorine, and was favorable even at low concentration of acid, whereas copper leaching increased with increase in concentration of acid and decrease in temperature. In a two-stage leaching process, copper was mostly dissolved (97%) in 165 min at 25 degrees C during the 1st stage leaching in 2.0 mol/L HCl by electro-generated chlorine at a current density of 714 A/m(2) along with a minor recovery of gold (5%). In the 2nd stage gold was mostly leached out (93% recovery, similar to 67 mg/L) from the residue of the 1st stage by the electrogenerated chlorine in 0.1 mol/L HCl. Gold recovery from the leach liquor by ion exchange using Amberlite XAD-7HP resin was found to be 95% with the maximum amount of gold adsorbed as 46.03 mg/g resin. A concentrated gold solution, 6034 mg/L with 99.9% purity was obtained in the ion exchange process. (C) 2011 Elsevier B.V.. All rights reserved.