The electrochemical behavior of Co(II) in urea-choline chloride-CoCl2 melt was investigated by cyclic voltammetry at 373 K. The results show that the reaction of Co(II) to Co is irreversible and it proceeds via a one-step two electrons transfer process. The diffusion coefficient of Co(II) was estimated to be 1.7 x 10(-6) cm(2) s(-1) at 373 K. Electrodeposition of cobalt was studied at different cathodic potentials (-0.80 to -0.95 V) and at different temperatures (353 to 383K) in eutectic mixture of choline chloride and urea (1:2 molar ratio). The deposits were characterized using scanning electron microscope (SEM), energy-dispersive spectroscopy (EDS), and X-ray diffraction (XRD). SEM images show that uniform, dense, and compact deposits were obtained at -0.80 V within a temperature range of 353 K to 373 K. EDS and XRD analysis confirm that high-purity metallic Co deposits were obtained. (C) 2014 Elsevier Ltd. All rights reserved.