Commercial carbon cloth made of PAN-based carbon fibres was used as free-standing anode for lithium intercalation. The role of surface functional groups on the specific irreversible charge loss and reversible charge during the intercalation and de-intercalation of lithium ions into carbon cloth has been investigated. Oxygen groups have been introduced by nitric acid vapour treatment and subsequently gradually removed by thermal treatment at different temperatures in He or H-2 atmosphere as confirmed by X-ray photoelectron spectroscopy. A clear correlation between the amount of surface-bound oxygen groups and the irreversible specific charge was observed. Three irreversible processes were distinguished during the first cathodic scan: (i) reduction of oxygen groups, (ii) formation of the solid electrolyte interphase (SEI) and (iii) presumably exfoliation. The latter one was only observed for samples with low surface oxygen concentration, and its contribution to the irreversible capacity was small due to the low graphitization degree of the samples. An increased specific reversible charge upon increasing the amount of oxygen-containing groups was observed with the main improvement above 1.5 V. (C) 2012 Elsevier Ltd. All rights reserved.