Swelling-agent-free synthesis of silica materials with large mesopores were developed using silicate from rice husk ash (RHA) as an alternative silica precursor in this study. Unlike the conventional methods for preparing large-pore silica materials in which toxic and expensive additives were employed as swelling agents, the obtained silica materials with large mesopores could be facilely prepared via a simple temperature-controlled approach without adding pore expanders. The fusion and hydrothermal temperature effects on the structural properties of obtained mesoporous silicas were investigated by the XRD, nitrogen adsorption-desorption, SEM and TEM analyses. The obtained mesoporous MS-400(25), which was fabricated using rice husk fused at 400 degrees C and treated with sodium hydroxide at 25 degrees C, exhibited bimodal meso-porosities (2.7 and 24 nm) and large pore volume (1.92 cm(3)/g). The bi-porosities mainly originated from the intra-particle mesostructure within silica particles and the inter-particle porosity between the aggregated nano-sized silica particles, respectively. The synthesized silicas were applied as the supports of adsorbents for CO2 capture. The adsorption tests clearly revealed that the tetraethylenepentamine (TEPA) impregnated MS-400(25) material could achieve CO2 adsorption capacity of 173 mg/g under 10% CO2 at 75 degrees C, which was the best sorbents among all samples due to its relatively large pore volume. (C) 2014 Elsevier B.V. All rights reserved.