Diffraction grating-based holographic images have been successfully replicated in biaxially oriented polypropylene (BOPP) shrink films through large-area roll-to-roll nanoimprint technique. Such hot embossing of holographic images on BOPP films represents a promising means of creating novel security features in packaging applications. The major limitation of the high-quality replication is the relatively large thermal shrinkage of BOPP shrink film. However, although an appropriate shrinkage is demanded after embossing, over-shrinking not only causes distortion in embossed images, but also reduces the various properties of BOPP shrink films mainly due to the disappearance of orientation. The effects of embossing temperature on the mechanical, thermal and optical properties as well as polymer surface morphologies were systematically analyzed. The results show that the optimal process parameters are listed as follows: the embossing temperature at 104-110 degrees C, embossing force 6 kg/cm(2) and film speed 32 m/min. The variation in flow behavior of polymer surface during hot embossing process is highly dependent on the temperature. In addition, the adhesion from the direct contact between the rubber press roller and polymer surfaces is suggested to cause the serious optical properties failure. (C) 2014 Elsevier B.V. All rights reserved.