Biological materials offer a wide range of multifunctional and structural properties that are currently not achieved in synthetic materials. Herein we report on the synthesis and preparation of bioinspired organic/inorganic composites that mimic the key physicochemical features associated with the mechanical strengthening of both squid beaks and mussel thread coatings using chitosan as an initial template. While chitosan is a well-known biocompatible material, it suffers from key drawbacks that have limited its usage in a wider range of structural biomedical applications. First, its load-bearing capability in hydrated conditions remains poor, and second it completely dissolves at pH < 6, preventing its use in mild acidic microenvironments. In order to overcome these intrinsic limitations, a chitosan-based organic/inorganic biocomposite is prepared that mimics the interfacial chemistry of squid beaks and mussel thread coating. Chitosan was functionalized with catechol moieties in a highly controlled fashion and combined with superparamagnetic iron oxide (gamma-Fe2O3) nanoparticles to give composites that represent a significant improvement in functionality of chitosan-based biomaterials. The inorganic/organic (gamma-Fe2O3/catechol) interfaces are stabilized and strengthened by coordination bonding, resulting in hybrid composites with improved stability at high temperatures, physiological pH conditions, and acid/base conditions. The inclusion of superparamagnetic particles also makes the composites stimuli-responsive.