Cotton fabrics were coated with arrays of ZnO hexagonal prisms using an electroless (catalytic/auto-catalytic) deposition process. A typical three step method, similar to those used for electroless deposition of metals on insulating substrates, consisting of pre-activation, activation and deposition steps was employed. The low-dimensional ZnO particles were grown from an aqueous solution containing zinc nitrate as source of zinc ions and dimethylamineborane as reducing agent. The as-obtained ZnO-coated cotton fabrics were characterized from the point of view of structure by X-ray diffraction (XRD) and morphology by scanning electron microscopy (SEM). The XRD studies demonstrate that the ZnO particles have a hexagonal wurtzite crystalline structure. The SEM observations prove that the cotton fibers are homogeneously covered by hexagonal prisms which have uniform base size of approximately 500 nm and height of 1 mu m. Optical spectroscopy measurements show that the functionalization with ZnO strongly decreases the transmittance in the UV vis region of the cotton fabrics. An important characteristic is that the ZnO-functionalized cotton fabrics exhibit superhydrophobicity, with water contact angles exceeding 150 degrees. The technique described is highly reproducible, easy scalable and cheap, allowing a wide range of applications. (C) 2012 Elsevier B.V. All rights reserved.