Low d. polyethylene was processed by multiple extrusion at 120-180 degrees C (up to 25 times) and studied for changes of mech. and thermal properties (tensile strength, hardness, softening temp., d., melting flow rate, melting enthalpy, mol. mass). A stepwise worsening the mech. strength and degrdn. of the polyethylene samples were obsd.