The electrical and rheological properties of an ethylene vinyl acetate (EVA) copolymer filled with bamboo charcoal were investigated. The composites were prepared by melt process in an internal batch mixer. Size distribution analysis showed that d((50)) and d((90)) values of the bamboo charcoal particles are 12.7 and 40 mu m, respectively, with a mean diameter of 22 mu m. Scanning electron microscopy proved that the particles of bamboo charcoal present a rectangular shape. The electrical percolation threshold was observed at 0.18 volume fraction (35 wt%) of bamboo. Beyond the percolation threshold, a considerable increase in electrical properties was observed up to a limit value of 10(-2) S/m. The rheological percolation was studied from different rheological models. As a result, the rheological percolation threshold was observed at 0.3 volume fraction (50 wt%) of bamboo charcoal contents. So, the electrical percolation occurs before the rheological percolation. This is principally due to the filler's characteristics such as the specific surface area, the aspect ratio, and the surface properties. Finally, the bamboo charcoal confers high electrical properties to the EVA composite without inducing strong changes in its viscoelastic properties.