Plasma treatments were applied on the surface of postconsumer polyethylene terephthalate (PET) bottles to increase their wettability and hasten the subsequent hydrolysis process. Sixty-four treatments were tested by varying plasma composition (oxygen and air), power (25130 W), pressure (50200 mTorr), and time (1 and 5 min). The best treatment was the one applied in air plasma at 130 W and 50 mTorr for 5 min, as it provided the lowest contact angle, 9.4 degrees. Samples of PET before and after the optimized plasma condition were subjected to hydrolysis at 205 degrees C. Although the treatment changed only a thin surface layer, its influence was evident up to relatively high conversion rates, as the treated samples presented more than 40% higher conversion rates than the untreated ones after 2 h of reaction. Infrared spectroscopy showed that the terephthalic acid obtained from 99% of depolymerization was similar to the commercial product used in PET synthesis. (c) 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 127: 1989-1996, 2013