Morpholine-functional homopolymers and copolymers (using 4-acryloylmorpholine (4AM), 2-N-morpholinoethyl acrylate (MEA) and 2-N-morpholinoethyl methacrylate (MEMA)) were synthesized by nitroxide mediated polymerization (NMP) and tested for aqueous thermo-responsiveness. MEA homopolymerizations and MEMA/9-(4-vinylbenzyl)-9H-carbazole (VBK) were controlled as evidenced by linear increases in number-average molecular weight, (M-n) over bar, versus conversion (X < 0.75) and relatively low polydispersities <(M-w)over bar>/(M-n) over bar, = 1.30 - 1.60. For MEMA/VBK copolymers, increases in copolymer (M-n) over bar, VBK content in the copolymer and polymer concentration in aqueous solution resulted in a decrease in the cloud point temperature, CPT (typically varied between 33.7 and 47.9 degrees C). 2-(dimethylamino)ethyl methacrylate (DMAEMA)/4AM copolymerizations were controlled when initial 4AM molar composition f(4AM,0) > 0.10; however, the resulting final copolymers exhibited a sharp and completely reversible CPT only when f(4AM,0) < 0.20. Poly(mEA) was water-soluble but was not thermo-responsive. (C) 2012 Elsevier Ltd. All rights reserved.