In this study, agave fiber/linear medium density polyethylene composites were manufactured by rotational molding. A laboratory scale biaxial machine was used, where the internal air temperature during the processing cycle was measured. Two sizes of agave fibers (50 and 100 mesh) were used separately and mixed together (50/50) at concentrations varying between 0 and 15 wt%. The initial mixtures were obtained by dry blending, rotomolded under different operation conditions (oven temperature, processing cycle time, and rotational speeds), and the final pieces were compared. For each process condition, a complete morphological analysis was performed to relate with mechanical properties in terms of tensile, impact, and flexural strength. The results show that there is an optimum fiber concentration around 10%, and blending fiber sizes gave better tensile properties than using each size alone. POLYM. ENG. SCI., 52:2489-2497, 2012. (C) 2012 Society of Plastics Engineers