Multilayer hard coatings of TiCN/TiC/TiN on high speed steel substrates were deposited using a chemical vapor deposition system. Evaluations of microstructure, wear morphology of coatings were characterized by scanning electron microscopy, and optical microscopy. Friction coefficient and wear rates of coatings were investigated using ball-on-disk tester sliding against a WC ball at a constant load of 20 N. Tribological behavior of the coatings at room and elevated temperature were discussed. Different changing tendency of friction coefficient were observed from ball-on-disc experiments. Results showed that the friction coefficient of coatings increased gradually to a highest value, then to a relatively constant value at room temperature dry sliding wear. The friction coefficient exhibited a reverse variation tendency at temperature of 550 degrees C. It got a higher value at the first sliding friction cycles. Then the value of friction coefficient decreased, suffered irregular oscillations and kept a relatively lower value with increasing sliding time. Reasons of the variation of friction coefficient with sliding time and wear mechanism were analyzed and discussed at room and elevated temperatures, respectively. (C) 2011 Elsevier B.V. All rights reserved.