Ferroelectric properties of ultrathin films of Nylon 11 were investigated. The thickness was in the range of 25 to 55 nm. Ferroelectric response was largely affected by thermal annealing and following cooling conditions. Thermal annealing at higher temperature followed by quenching in liquid nitrogen gave larger remanent polarization and smoother surface, whereas cooling down in an ambient atmosphere caused smaller remanent polarization and rough surface. Surface roughness strongly affected the polarization reversal and remanent polarization. Hydrogen bonding in crystal was also significantly related to the polarization reversal and thus remanent polarization. (C) 2009 Elsevier B.V. All rights reserved.