We synthesized the thiophene-based copolymers (P(3TAF-co-3TAa)-A-n and P(3TAF-co-3TAa)-B-n) using two different kinds of thiophene monomers, (N-(3-thienylmethylene)-2-aminofluorene and 3-thiophene acetic acid), as sensitizers on the DSSCs. P(3TAF-co-3TAa)-A-n (n=1, 2, 3) was synthesized with different molar ratios (3TAF:3TAa=1:5, 1:10, 1:20) of monomers at room temperature, respectively. Also, P(3TAF-co-3TAa)-B-n (n=1, 2, 3) was synthesized with above molar ratios of monomers at 0 degrees C, respectively. The DSSCs devices were fabricated using the thiophene-based copolymers as sensitizers and their photovoltaic performances were measured by using a solar simulator under AM 1.5. In the DSSCs devices using polymeric sensitizers, V-oc is 0.53-0.60 V, J(sc) is 1.9-4.5 mA/cm(2), FF is 0.51-0.63 and the power conversion efficiency is 0.63-1.53%, respectively. (c) 2010 Elsevier B.V. All rights reserved.