In this work, we report the morphological and electrochromic properties of electrochemically synthesized polyaniline (PANI) thin films on bare and modified indium-tin oxide (ITO) glass substrates. In the last case, the surface of ITO glass was covered by a self-assembled monolayer of N-phenyl-gamma-aminopropyl-trimethoxysilane (PAPTS). Atomic force microscopy images and perfilometry show that smoother and thinner PANI films were grown on PAPTS-modified ITO substrates. PANI-based electrochromic devices (ECDs) were assembled by using a viscous polymeric electrolyte (PE) of LiClO(4) and polymethyl methacrylate (PMMA) co-dissolved in a mixture of propylene and ethylene carbonate. The architectural design of the devices was glass/ITO/PANI/PE/ITO/glass. A dual ECD was also prepared by collocating a poly(3-methylthiophene) (P3MT) thin film as a complementary electrochromic element. The effect of the PAPTS-modified ITO substrate is reflected in a higher optical transmittance at bleach state and a little less color change at 550 nm of PANI-based ECDs. (c) 2007 Elsevier B.V. All rights reserved.