The morphology and bulk properties of microporous membranes based on poly (ether ether ketone) (PEEK) have been investigated as a function of initial casting composition and thermal and mechanical processing history. Membranes were prepared via solid-liquid phase separation of miscible blends of PEEK and polyetherimide (PEI), with subsequent extraction of the PEI diluent. Scanning electron microscopy studies revealed a microporous morphology with two distinct pore size scales corresponding to diluent extraction from interfibrillar and interspherulitic regions, respectively. The membrane structure was sensitive to both initial blend composition and crystallization temperature, with the resulting pore size distribution reflecting the kinetics of phase separation. For membranes prepared with lower initial diluent content or at lower crystallization temperatures, mercury intrusion porosimetry indicated a relatively narrow distribution of fine interfibrillar pores, with an average pore size of approximately 0.04 microns. Membranes prepared at higher diluent content or at higher crystallization temperatures displayed a broad pore distribution, with a sizeable population of coarse, interspherulitic pores (0.1 to 1 mu m in size). Uniaxial drawing led to a fibrillated network structure with markedly higher water flux characteristics compared to the as-cast membranes.