Unmodified blends of two thermoplastic polyurethanes (TPU) and six polyolefines were used to study the influence of the component viscosities on the blend morphology and mechanical properties. Blends were produced by melt mixing using a twin screw extruder. Interactions between the blend components could not be detected by DSC, DMA, selective extraction, and SEM micrographs of cryofractures. The variation in tensile strength with blend composition produce a U-shaped curve with the minimum between 40 and 60 wt % of polyolefine. At similar viscosity ratios (eta(d)/eta(m)), blends with polyether based TPU(TPU-eth) have a finer morphology than blends with polyester based TPU (TPU-est). This is due to the lower surface free energy of the polyether soft segments compared to the polyester soft segments. Different morphologies also lead to changes in mechanical behavior. Blends with TPU-eth show a lower decrease in tensile strength with blend composition than blends with TPU-est. The viscosity ratio between TPU and polyolefines can be directly correlated to the blend morphology obtained under similar blending conditions. TPU/PE blends show a lower dispersity than TPU/PP blends, due to the higher viscosity ratios of TPU/PE blends. This results in a greater reduction in tensile strength with the disperse phase content.