High-temperature molding of Brabender-mixed blend of polyacrylic acid (PAA) and epoxidized natural rubber (ENR) causes thermally induced crosslinking between PAA and ENR. Studies on Monsanto rheometry of the blend and physical properties, solvent swelling, and dynamic mechanical properties of the molded blend show that both mixer rotor speed and carbon black filler influence the crosslinking between the component polymers. For example, the extent of crosslinking for the 50-50 PAA-ENR blend was found maximum when the component polymers were mixed at 40 rpm, but the same blend filled with 30 phr HAF carbon black filler showed maximum crosslinking when mixing was carried out at 120 rpm. The results have been explained on the basis of formation of network on the filler surface, which in turn depends on two competing factors : increase in bound rubber formation with increase in filler loading at a fixed rotor speed and enhanced degradation of ENR at higher mixer rotor speed at a fixed filler loading.