Undoped and Eu-doped yttrium aluminum garnet nano-powders were prepared by a facile combustion method with citric acid/ethylene diamine tetraacetic acid (EDTA) as fuels and nitrates as oxidizers. The precursors and powders calcined at 1030 degrees C were investigated using thermogravimetric (TG), differential thermal analysis (DTA). X-ray diffraction (XRD), scanning electron microscope (SEM), and Brunauer-Emmett-Teller (BET) surface area measurements. It was found that the powders could be indexed with a garnet structure. The grains were in shape of hemispherical with sizes between 60 nm and 100 nm. With decreasing the citric acid/EDTA ratio, the crystallite size decreased steadily and the specific surface area increased. Investigations of photoluminescence (PL) revealed that as-synthesized YAG:Eu3+ phosphor samples exhibited an orange emission band with a main peak at 591 nm under the excitation of 394 nm. As citric acid amounts increased, the quality of crystallinity became higher and the luminescent properties were monotonously enhanced. (C) 2010 Elsevier Ltd. All rights reserved.