The microwave characteristics and the microstructures of 0.88Al(2)O(3)-0.12TiO(2) with various amounts of MgO-CaO-SiO2-Al2O3 (MCAS) glass sintered at different temperatures have been investigated. The sintering temperature can be lowered to 1300degreesC by the addition of MCAS glass. The densities, dielectric constants (e,) and quality values (Q x f) of the MCAS-added 0.88Al(2)O(3)-0.12TiO(2) ceramics decrease with the increase of WAS glass content. The temperature coefficients of the resonant frequency (tau(f)) are shifted to more negative values as the WAS content or the sintering temperatures increase. The change of the crystalline phases of Al2TiO5 phase and rutile-TiO2 phase has profound effects on the microwave dielectric properties of the MCAS-added Al2O3TiO2 ceramics. As sintered at 1250degreesC, 0.88Al(2)O(3)-0.12TiO(2) ceramics with 2 wt.% WAS glass addition exists a e, value of 8.63, a Q x f value of 9578 and a tau(f) value of +5 ppm/degreesC. (C) 2003 Elsevier Science Ltd. All rights reserved.