Journal of the American Ceramic Society, Vol.93, No.10, 2929-2931, 2010
Lift-Off PMN-PT Thick Film for High-Frequency Ultrasonic Biomicroscopy
Piezoelectric 0.65Pb(Mg(1/3)Nb(2/3))O(3)-0.35PbTiO(3) (PMN-35PT) thick film with a thickness of approximately 12 mu m has been deposited on the platinum-buffered Si substrate using a sol-gel composite method. The separation of the film from the substrate was achieved using a wet chemical method. The lifted-off PMN-35PT thick film exhibited good dielectric and ferroelectric properties. At 1 kHz, the dielectric constant and the dielectric loss were 3326 and 0.037, respectively, while the remnant polarization was 30.0 mu C/cm2. A high-frequency single-element acoustic transducer fabricated with this film showed a bandwidth at -6 dB of 63.6% at 110 MHz.